Rheological properties of dental resin cements during polymerization

Abstract

PURPOSE. The purpose of this study was to observe the change of viscoelastic properties of dental resin cements during polymerization.

MATERIALS AND METHODS. Six commercially available resin cement materials (Clearfil SA luting, Panavia F 2.0, Zirconite, Variolink N, RelyX Unicem clicker, RelyX U200) were investigated in this study. A dynamic oscillation-time sweep test was performed with AR1500 stress controlled rheometer at 32 degrees C. The changes in shear storage modulus (G‘), shear loss modulus (G‘’), loss tangent (tan delta) and displacement were measured for twenty minutes and repeated three times for each material. The data were analyzed using one-way ANOVA and Tukey’s post hoc test (a=0.05).

RESULTS. After mixing, all materials demonstrated an increase in G‘ with time, reaching the plateau in the end. RelyX U200 demonstrated the highest G’ value, while RelyX Unicem (clicker type) and Variolink N demonstrated the lowest G‘ value at the end of experimental time. Tan delta was maintained at some level and reached the zero at the starting point where G’began to increase. The tan delta and displacement of the tested materials showed similar pattern in the graph within change of time. The displacement of all 6 materials approached to zero within 6 minutes.

CONCLUSION. Compared to other resin cements used in this study, RelyX U200 maintained plastic property for a longer period of time. When it completed the curing process, RelyX U200 had the highest stiffness. It is convenient for clinicians to cement multiple units of dental prostheses simultaneously.

연구 목적: 본 연구의 목적은 중합 과정 중 치과용 레진 시멘트의 점탄성 성질의 변화를 관찰하기 위한 것이다.

연구 재료 및 방법:: 6 종류의 레진시멘트(Clearfil SA luting, Panavia F 2.0, Zirconite, Variolink N, RelyX Unicem clicker, RelyX U200)가 이번 실험에 사용되었다. AR1500 stress controlled rheometer를 이용해 32 도에서 동적 시간 경과 시험(dynamic oscillation time sweep test)이 시행되었다. 각각의 레진시멘트의 전단 저장 계수(G‘), 전단 손실 계수(G’‘), 손실 탄젠트(tan delta), 변위량을 20분 동안 3번씩 반복 측정하였다. 측정 결과는 일원배치분석 및 Tukey‘s hoc test로 사후 검정을 시행하였다(a=0.05).

결과: 모든 레진 시멘트는 혼합 후 시간에 따라 G’ 값이 증가하였고, 최종적으로 안정상태에 도달하였다. 실험 종료 시점에서 RelyX U200은 가장 높은 G‘값을 나타냈고, RelyX Unicem (clicker type)과 Variolink N이 가장 낮은 G‘값을 나타냈다. Tan delta와 변위량은 일정 수준의 값을 유지하다가 G’이 증가하기 시작하는 시점에서 0에 도달하였다. 이는 변위량이 0에 도달하는 지점과 거의 일치하였으며, 그 시간은 6분 내외였다.

결론: 본 연구에서 RelyX U200은 다른 레진 시멘트와 비교하여 가장 오랜 시간 동안 소성을 유지하고, 경화 완료 후 가장 높은 강도(rigidity)를 보였다. 따라서 여러 개의 보철물을 동시에 합착해야 하는 경우에 RelyX U200이 유용할 것으로 사료된다.